Influence of Moisture Content and Wet Environment on the Fatigue Behaviour of High-Strength Concrete

verfasst von: Mohamed Abubakar Ali, Christoph Tomann, Fadi Aldakheel, Markus Mahlbacher, Nima Noii, Nadja Oneschkow, Karl Heinz Drake, Ludger Lohaus, Peter Wriggers, Michael Haist
Abstract: The influence of a wet environment on the fatigue behaviour of high-strength concrete has become more important in recent years with the expansion of offshore wind energy systems. According to the few investigations documented in the literature, the fatigue resistance of specimens submerged in water is significantly lower compared to that of specimens in dry conditions. However, it is still not clear how the wet environment and the moisture content in concrete influence its fatigue behaviour and which damage mechanisms are involved in the deterioration process. Here the results of a joint project are reported, in which the impact of moisture content in concrete on fatigue deterioration are investigated experimentally and numerically. Aside from the number of cycles to failure, the development of stiffness and acoustic emission (AE) hits are analysed as damage inductors and discussed along with results of microstructural investigations to provide insights into the degradation mechanisms. Subsequently, an efficient numeric modelling approach to water-induced fatigue damage is presented. The results of the fatigue tests show an accelerated degradation behaviour with increasing moisture content of the concrete. Further, it was found that the AE hits of specimens submerged in water occur exclusively close to the minimum stress level in contrast to specimens subjected to dry conditions, which means that additional damage mechanisms are acting with increasing moisture content in the concrete.
Organisationseinheit(en): Institut für Baustoffe
Institut für Kontinuumsmechanik
Externe Organisation(en): LPI Ingenieurgesellschaft mbH
Swansea University
Typ: Artikel
Journal: MATERIALS
Band: 15
ISSN: 1996-1944
Publikationsdatum: 28.01.2022
Publikationsstatus: Veröffentlicht
Peer-reviewed: Ja
ASJC Scopus Sachgebiete: Allgemeine Materialwissenschaften, Physik der kondensierten Materie
Elektronische Version(en): https://doi.org/10.3390/ma15031025 (Zugang: Offen)
: Details im Forschungsportal „Research@Leibniz University“

BibTeX

@article{9ca5b76a5ce246a5882c906cb9825730,
title = "Influence of Moisture Content and Wet Environment on the Fatigue Behaviour of High-Strength Concrete",
abstract = "The influence of a wet environment on the fatigue behaviour of high-strength concrete has become more important in recent years with the expansion of offshore wind energy systems. According to the few investigations documented in the literature, the fatigue resistance of specimens submerged in water is significantly lower compared to that of specimens in dry conditions. However, it is still not clear how the wet environment and the moisture content in concrete influence its fatigue behaviour and which damage mechanisms are involved in the deterioration process. Here the results of a joint project are reported, in which the impact of moisture content in concrete on fatigue deterioration are investigated experimentally and numerically. Aside from the number of cycles to failure, the development of stiffness and acoustic emission (AE) hits are analysed as damage inductors and discussed along with results of microstructural investigations to provide insights into the degradation mechanisms. Subsequently, an efficient numeric modelling approach to water-induced fatigue damage is presented. The results of the fatigue tests show an accelerated degradation behaviour with increasing moisture content of the concrete. Further, it was found that the AE hits of specimens submerged in water occur exclusively close to the minimum stress level in contrast to specimens subjected to dry conditions, which means that additional damage mechanisms are acting with increasing moisture content in the concrete.",
keywords = "Acoustic emissions analysis, Fatigue deterioration, High-strength concrete, Microscopic material model, Moisture content, Phase-field approach, Porous media theory, Water-induced degradation mechanisms",
author = "Ali, {Mohamed Abubakar} and Christoph Tomann and Fadi Aldakheel and Markus Mahlbacher and Nima Noii and Nadja Oneschkow and Drake, {Karl Heinz} and Ludger Lohaus and Peter Wriggers and Michael Haist",
note = "Funding Information: Funding: This research was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation)—Project numbers (353757395) (HA 7917/7-2 | LO 751/22-2 | WR 19/58-2) within the Priority Programme 2020 {\textquoteleft}Cyclic Deterioration of High-Performance Concrete in an Experimental-Virtual Lab{\textquoteright}. Parts of the experimental investigation were funded by the Federal Ministry for Economic Affairs and Climate Action within the project WinConFat—Project number (0324016A). Funding Information: Acknowledgments: The authors thank the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation) and the Federal Ministry of Economic Affairs and Energy for funding the research projects.",
year = "2022",
month = jan,
day = "28",
doi = "10.3390/ma15031025",
language = "English",
volume = "15",
journal = "MATERIALS",
issn = "1996-1944",
publisher = "MDPI AG",
number = "3",
}